塑料单位换算表

时间：2017-05-11

塑料单位换算表

抗折、抗张、耐压缩强度及模数
MPa	Psi	kg/cm2	kg/m2
1	145	10.19	101945.15
6.9×10-3	1	0.0703	703.07
9.8×10-2	14.22	1	10000
9.8×10-6	1.422.×10-3	0.0001	1

冲击强度
ft-lb/in	J/m	kg-cm/cm
1	53.35	5.45
0.0187	1	0.102
0.183	9.803	1

英制 (British)	米制 (Metric)	国际制 (SI Metric)
1 ft	=0.3048 m
1 in	=2.54cm	=25.4mm
1 thou	=0.0254 mm	=25.4μm
1 yd2	=0.8361 m2
1 ft2	=0.0929 m2
1 in2	=6.4516 cm2	=654.16 mm2
1 yd3	=0.7645 m3
1 ft3	=0.0283 m3	=28.317 dm3
1 in3	=16.387 cm3
1 gal	=4.5459 litres	=4.5459 dm3
℉	=(1.8×℃)+32
1 ton	=1.0160 tomes
1 lb	=0.4536 kg
1 oz	=28.3495 g
1 lbf	=0.457 kgf	4.4482 N
1 lbf/in2	=0.0703kgf/cm2	=6.8948kN/m2
1 lb/ft3	=16.018 kg/m3
1 lb/in3	=27.68 g/cm3	=27.68 Mg/m3
1 Btu	=251.996 cal	=1.0550 KJ

米制(Metric)	英制 (British)	国际制 (SI Metric)
1 m	=3.2808 ft
1 cm	=0.3937 in
1 mm	=0.03937 in
1 m2	=1.1959 yd2
1 m2	=10.7639 ft2
1 cm2	=0.1550 in2
1 m3	=1.3079 yd3
1 m3	=35.3147 ft3
1 cm3	=0.061 in3
1 litre	=0.2199 gal	=1 dm3
1 cm3	=0.0000353 ft3
℃	=((℉-32)×5)÷9
1 tonne	=0.9842 ton
1 kg	=2.2046 lb
1 g	=0.0353oz
1 kgf	=2.2046 lbf	=9.8066 N
1 kgf/cm2	=14.2233 lbf/in2	=98.0665kN/m2
1 kg/m3	=0.0624 lb/ft3
1 g/cm3	=0.0361 ib/in3

词条
词条说明
售后服务
为创造**，提高企业**度，树立企业形象，我公司本着，一切追求高质量，用户满意为宗旨。的精神，以较优惠的价格，较周到的服务，较可靠的产品质量，的原则向您郑重承诺：一、产品质量承诺： 1、产品的质量检测资料。UL认证，***报告，MSDS等…… 2、产品均属原厂原包——假一赔十，待客户被确认规格型号再发货。二、产品价格承诺： 1、为了保证原材料的质量稳定性，均选用国内或进口优质**产品。
POM的特点及用途
Delrin均聚聚甲醛系列树脂与其它聚甲醛产品系列相比，具有更高的分子量。这些高性能均聚甲醛的这种标识性特征，以及**的高结晶度，使材料具有以下特点：韧性，高冲击强度，高耐反复冲击性和*冲击改性就具有的高延展性。不需要填料/增强或其他改性就具有的高机械强度和刚度， **的耐蠕变和长期耐疲劳性。在高粘性这些高机械强度和韧性的特性，可以从高粘度Delrin均聚甲
注塑制品出现水纹的原因分析
注塑制品出现水纹的原因分析注塑制品水纹，包括表面气泡和内部气孔。造成缺陷的主要原因是气体（主要有水汽、分解气、溶剂气、空气）的干扰。具体原因分析如下： 1.机台方面：（1）料筒、螺杆磨损或过胶头、过胶圈存在料流死角，长期受热而分解。（2）加热系统失控，造成温度过高而分解，应检查热电偶、发热圈等加热元件是否有问题。螺杆设计不当，造成个解或容易带进空气。 2.模具方面：（1）排气不良。（2
聚甲醛(POM)加工注射成型工艺
聚甲醛(POM)注射成型工艺 POM（又称赛钢、特灵）。它是以甲醛等为原料聚合所得。POM-H（聚甲醛均聚物），POM-K（聚甲醛共聚物）是高密度、高结晶度的热塑性工程塑料。具有良好的物理、机械和化学性能，尤其是有优异的耐摩擦性能。 POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度**过一定限度或熔体受热时间过长，会引起分解。铜是POM降解催化剂，与POM熔体接触的部位应避免